Mineralizer (moisture wicking)
MINERALIZING / silicate solution to FIX Damp
Create internal barriers against moisture and n concrete walls, stone, brick, ect .. consolidates the surface.
Reacts inside the support, by a process of silidificación, solidifying loose parts by moisture.
Mineraliser to inject WALLS with rising damp.
BUY MINERALIZING or liquid to be injected into the walls to troubleshoot CAPILLARY RISING HUMIDITY
Mineralizing BUY FOR WALLS WITH Damp
IF YOU WANT TO KNOW MORE ABOUT THE HUMIDITY by capillary action, and how to fix YOURSELF, CLICK HERE
This mineralizing comprises a potassium silicate and a potassium methyl siliconate.
Both products react with atmospheric CO2 giving potassium carbonates.
Potassium silicate to react with atmospheric CO2, is deposited on the capillary wall a layer of silica narrow capillary diameter, offering greater difficulty of passing moisture.
Moreover, by reacting with potassium methyl siliconate form polimetilsilano atmospheric CO2 serving as avoiding rise repellent moisture that may penetrate into these capillaries.
NATURE OR COMPOSITION MINERALIZING
Formulated aqueous solution based on highly stabilized potassium silicate.
Consolidate the surface.
· Form an internal barrier in the wall against moisture.
Reacts inside the wall, through a process of silidificación.
· Solidifies loose parts by moisture.
WHERE CAN I USE THE MINERALIZING TO CREATE BARRIERS AGAINST RISING Rising Damp?
It is used to strengthen and create internal moisture barriers in concrete walls, stone, brick, etc ..
The mineralizer is a double-acting liquid product
Applied Surface is waterproof and water repellent to prevent the advance of the moisture by capillarity in mineral substrates.
Usable in porous materials such as concrete, brick, cement, stone, etc., where there is an incorrect isolation from the surrounding soil and thus, direct contact of moisture through the construction material.
Depth applied through holes in the wall where the product by pressure or gravity is injected, having a first capillary constrictor effect, reducing its diameter by precipitation of crystalline silica.
This narrowing is also combined with a repellent effect of humidity which, together, prevent the passage of liquid water while still remaining permeable to water vapor.
On very porous substrates may surface application (without holes), considering that the penetration will be much lower and that the final effect will be more superficial, mainly consolidating and waterproof.
The main property of Mineralizing Agent is to consolidate the surface and form an internal moisture barrier. Reacts inside the support, by a process of silidificación, solidifying loose parts by moisture.
HOW mineralizing APPLIES TO SOLVE PROBLEMS Damp?
Injection is applied in the form of supply (USE, NOT THIN)
For application by brush, roller or spray: 1/1 potential dilution with water and a subsequent rinsing to drag the superficial excesses and avoid depositions.
The surface should be clean, dry and free of dust, grease, salt and other contaminants.
PREPARING THE WALL
The walls must contain less than 50-70% moisture. Otherwise injections will not be effective. Therefore they must be performed in periods where the walls are drier.
Depending on the material of the wall, the hole locations will be different:
POROUS BRICK WALLS: Holes the brick itself can be made both, as in the joints.
NO POROUS BRICK WALLS: The holes must be made at the joints.
SANDSTONE WALLS OR POROUS: The holes are made in the same stone.
Piedro NONPOROUS WALLS: The holes will be made at the joints.
1. Drill holes (see drawing)
Alternative hole diameter Ø = 1.6-1.8 cm in two separate rows together in practice is 15 cm.
The spacing between these holes can vary between 12 and 15 cm (about 6 openings per lineal meter).
The inclination of the holes must be made between 30 and 45
The depth of the holes should be 2/3 the wall thickness. For very thick walls (50 cm) holes must be made on both sides.
2. Clean the holes once made.
3. Fill several times with mineralizing, the times necessary for 24 hours. (20-40 liters per meter in the case of walls with 20% absorption) by gravity.
In the case of insert injection pressure, the device should work from 0.5 to 20 bar. (High pressure can make the mineralizer by the boards.
4. Plugging the holes with conventional mortar and plastering again if necessary.
Product applied on the surface: Between 8 and 10 m2 x Liter
Performing a test is recommended to determine roughly consumption.
Consumption horizontal waterproofing of walls, under gravity or pressure is approximately 20 ± 5 liters per square meter of cross section of wall.
This consumption depends on the type of material (concrete, brick, stone, etc.) and the specific composition of it.
CONDITIONS OF SUPPORT
The temperature of the wall will 5-35º.
Depending on environmental conditions, access to CO2, etc., the notice waterproofing between one and three months after application.
It is recommended to carry out tests on the supports in order to observe possible changes of hue.
HEALTH AND SAFETY
No special precautions regarding toxicity. non flammable.
It comes in packs of 5 liters and 25 liters
ANGAR paintings, SC is not responsible for the problems caused by incorrect application of products
- Theoretical performance
- Between 8 and 10 square meters per Kilo and Hand (Depending on the media, whether it is new or already painted)
- Temperature of Application
- Do not apply below 5 ° Celsius
- 1.20 - 1.25 grs / cm3